1、重慶大學碩士學位論文過共晶Al-28wt.%Si活塞合金的研究姓名:吳玉露申請學位級別:碩士專業(yè):材料加工工程指導教師:李華基2010-04重慶大學碩士學位論文 英文摘要 II ABSTRACT As an important cast alloy, hypereutectic Al- Si alloy has low expansion coefficient and density, good cast
2、 performance and wear resistance. With the increase of silicon content, the alloy has a further decrease of linear expansion coefficient but further increase of wear resistance and heat resista
3、nce. However, the increased silicon content alloy has a large number of coarse and irregular lumps primary silicon and needle- like eutectic silicon, which seriously decrease the comprehensive pe
4、rformance of the alloy. So,refining its microstructure is a necessary way of improving comprehensive performance of the alloy.On the basis of the single modification of P、RE、Sr elements to the alloys, i
5、nvestigated the effect of modification on the structure and morphology of primary and eutectic silicon and discussed its modification mechanism;Used the orthogonal test to carry through the P - R
6、E- Sr triplex modification of the alloys and gained an efficient P- RE- Sr triplex modifier. Then made use of triplex modifier to modifiy the hypereutectic Al- 28wt.%Si alloy ,its average size of
7、 the primary silicon was only about 25µm. and made the primary silicon obtuse and nodular.gained the fine size 、 short bacilliform or vermiform eutectic silicon at the same time.Through no
8、rmal experiment measure、 maximal dispersion and curvilinear regression analysis investigated the effect of the various addition of P, RE on the room temperature tensile strength after heat treatm
9、ent、high temperature tensile strength at 300℃ and the hardness of the hypereutectic piston Al- 28wt.%Si alloy,confirmed the best composition extent for the modification. And elicited the following
10、conclusion:under the defined composition of alloy ,and with the adiition of P, RE, Sr elements were changed in the defined extent.the value of the room temperature tensile strength after heat treatme
11、nt is from 217.034 to 234.173MPa, high temperature tensile strength at 300℃ is from 122.839 to 129.045MPa, and the hardness is from 155.52 to 161.83. totally fufilled the capability requrement of piston al
12、loy. the research results may offer a new and helpful approach to improve piston alloys’ comprehensive performance at all times and extend its application extent ,so the results have considerable
溫馨提示
- 1. 本站所有資源如無特殊說明,都需要本地電腦安裝OFFICE2007和PDF閱讀器。圖紙軟件為CAD,CAXA,PROE,UG,SolidWorks等.壓縮文件請下載最新的WinRAR軟件解壓。
- 2. 本站的文檔不包含任何第三方提供的附件圖紙等,如果需要附件,請聯(lián)系上傳者。文件的所有權益歸上傳用戶所有。
- 3. 本站RAR壓縮包中若帶圖紙,網(wǎng)頁內(nèi)容里面會有圖紙預覽,若沒有圖紙預覽就沒有圖紙。
- 4. 未經(jīng)權益所有人同意不得將文件中的內(nèi)容挪作商業(yè)或盈利用途。
- 5. 眾賞文庫僅提供信息存儲空間,僅對用戶上傳內(nèi)容的表現(xiàn)方式做保護處理,對用戶上傳分享的文檔內(nèi)容本身不做任何修改或編輯,并不能對任何下載內(nèi)容負責。
- 6. 下載文件中如有侵權或不適當內(nèi)容,請與我們聯(lián)系,我們立即糾正。
- 7. 本站不保證下載資源的準確性、安全性和完整性, 同時也不承擔用戶因使用這些下載資源對自己和他人造成任何形式的傷害或損失。
最新文檔
- 過共晶al20wt.﹪si合金的復合變質(zhì)研究
- 過共晶Al-Si合金對Al-Si合金的變質(zhì)作用.pdf
- Bi合金化過共晶Al-Si合金的研究.pdf
- 過共晶Al--Si合金凝固組織研究.pdf
- 過共晶Al-Si合金無容器凝固.pdf
- 多層噴射沉積過共晶Al-Si合金的研究.pdf
- 過共晶Al-20%Si合金Si相形態(tài)的演變及性能研究.pdf
- CDS鑄造過共晶Al-Si合金組織及性能的研究.pdf
- 過共晶Al-24%Si合金的變質(zhì)及變質(zhì)機理研究.pdf
- 固液混合鑄造過共晶Al-Si合金的研究.pdf
- 過共晶Al-Si合金的半固態(tài)組織與Si相細?;芯?pdf
- 過共晶AL-Si合金熔體熱處理工藝的研究.pdf
- 過共晶鋁硅活塞合金的研究.pdf
- 近共晶鑄造Al-Si合金共晶凝固過程的研究.pdf
- 過共晶Al-Si合金受控擴散凝固行為及擠壓成形研究.pdf
- 利用組織遺傳性雙重變質(zhì)過共晶Al-Si合金的研究.pdf
- 過共晶Al-Si合金微觀組織結(jié)構(gòu)及摩擦磨損性能的研究.pdf
- 硼對過共晶Al-Si合金中初晶Si細化作用的研究.pdf
- al50wt.%si合金熔配工藝研究
- 電場下Al-Si、Al-Cu共晶合金凝固規(guī)律的研究.pdf
評論
0/150
提交評論