1、中文 中文 6800 字, 字,4100 單詞, 單詞,2.2 萬英文字符 萬英文字符出處: 出處:Decker C, Lorinczova I. UV-Radiation curing of waterborne acrylate coatings[J]. Jct Research, 2004, 1(4):247-256.外文文獻翻譯學(xué) 院 專 業(yè) 導(dǎo) 師
2、 學(xué) 生 學(xué) 號 2based UV-cured coatings have been shown to combine the flexible properties of high molecular weight polymers with the hardness of cross linked acrylate po
3、lymers. The potential of water- based resins and their performance in UV-radiation curing has already been investigated. They proved particularly well suited to be used as screen inks and protective coatings for plastic
4、s, paper, and wood. We report here a new study on the high speed UV-curing of some commercial water-based acrylate coatings, by focusing on the influence of the photo initiator and the functionalized oligomer on the pol
5、ymerization kinetics, namely cure speed and cure extent. The effect of the kind of water-based resin used (dispersion or emulsion) on the visco elastic properties of the UV-cured polymer will also be investigated, as we
6、ll as the correlation existing between the degree of conversion and the polymer properties, in particular its hardness.EXPERIMENTALMaterialsThe UV-curable waterborne formulations used in this study consisted of aqueous
7、emulsions or dispersions of acrylate functionalized oligomers containing a water soluble or water dispersible radical-type photo initiator. The compatibility of the initiator with the aqueous formulation and with the dri
8、ed coating is essential to achieve its uniform distribution in the sample. Two types of photo cleavable photo initiators were used in this study:(1) Oil-soluble photoinitiators which are partly soluble in water: Darocur
9、 1173 and Irgacure 2959 from Ciba Specialty Chemicals, and Lucirin TPO-L from BASF;(2) Oil-soluble photoinitiators which were dispersed in water: Irgacure 819 DW from Ciba Specialty Chemicals, and Esacure KIP/EM from
10、 Fratelli-LambertiThe chemical formulas of these photo initiators are given in Figure . They consist either of hydroxyl phenyl ketones or of acylphosphine oxides, which generate upon UV-exposure benzoyl radicals and eith
11、er alkyl radicals or phosphinoyl radicals,.RespectivelyThe waterborne resin was made of a short acrylate endcapped polymer chain containing either a few carboxylate groups to be dispersible in water or an added emulsifi
12、er. The characteristics of the five acrylate oligomers tested, all from BASF, and their acrylate content are given below.The water content was 50 wt% for the emulsions and60 wt% for the dispersions.Drying and UV CuringT
13、he formulation containing typically 1 wt% of photoinitiator was cast onto a barium fluoride crystal or a glass plate to obtain, after drying at 80°C, a 20-μm thickcoating. The sample was cured on a UV line (IST Min
14、icure, 80 W/cm) at a speed ranging between 5 and 60 m/min, at an incident light intensity of 500 mW cm. The UV dose received by the sample at each pass was measured by radiometry (International Light IL-390 radiometer)
溫馨提示
- 1. 本站所有資源如無特殊說明,都需要本地電腦安裝OFFICE2007和PDF閱讀器。圖紙軟件為CAD,CAXA,PROE,UG,SolidWorks等.壓縮文件請下載最新的WinRAR軟件解壓。
- 2. 本站的文檔不包含任何第三方提供的附件圖紙等,如果需要附件,請聯(lián)系上傳者。文件的所有權(quán)益歸上傳用戶所有。
- 3. 本站RAR壓縮包中若帶圖紙,網(wǎng)頁內(nèi)容里面會有圖紙預(yù)覽,若沒有圖紙預(yù)覽就沒有圖紙。
- 4. 未經(jīng)權(quán)益所有人同意不得將文件中的內(nèi)容挪作商業(yè)或盈利用途。
- 5. 眾賞文庫僅提供信息存儲空間,僅對用戶上傳內(nèi)容的表現(xiàn)方式做保護處理,對用戶上傳分享的文檔內(nèi)容本身不做任何修改或編輯,并不能對任何下載內(nèi)容負(fù)責(zé)。
- 6. 下載文件中如有侵權(quán)或不適當(dāng)內(nèi)容,請與我們聯(lián)系,我們立即糾正。
- 7. 本站不保證下載資源的準(zhǔn)確性、安全性和完整性, 同時也不承擔(dān)用戶因使用這些下載資源對自己和他人造成任何形式的傷害或損失。
最新文檔
- [雙語翻譯]--外文翻譯--紫外線固化水性丙烯酸酯涂料
- [雙語翻譯]--外文翻譯--紫外線固化水性丙烯酸酯涂料(英文)
- 紫外線固化水性丙烯酸酯涂料
- 2004年--外文翻譯--紫外線固化水性丙烯酸酯涂料
- 2004年--外文翻譯--紫外線固化水性丙烯酸酯涂料.doc
- 2004年--外文翻譯--紫外線固化水性丙烯酸酯涂料(英文).pdf
- 水性紫外光固化聚氨酯丙烯酸酯.pdf
- 合成表征水性光固化聚氨酯丙烯酸酯涂料
- 合成表征水性光固化聚氨酯丙烯酸酯涂料
- 紫外光固化聚氨酯丙烯酸酯涂料.pdf
- 合成表征水性光固化聚氨酯丙烯酸酯涂料.pdf
- 合成表征水性光固化聚氨酯丙烯酸酯涂料.doc
- 合成表征水性光固化聚氨酯丙烯酸酯涂料.doc
- 合成表征水性光固化聚氨酯丙烯酸酯涂料.pdf
- 高固體含量光固化水性聚氨酯丙烯酸酯涂料.pdf
- 水性丙烯酸酯改性聚氨酯用作光固化涂料的研究.pdf
- UV固化水性聚氨酯丙烯酸酯樹脂.pdf
- 環(huán)氧丙烯酸酯和聚氨酯丙烯酸酯預(yù)聚物及其水性光固化涂料的制備與改性.pdf
- 聚氨酯-丙烯酸酯水性木器涂料配方研究.pdf
- 紫外光固化環(huán)氧丙烯酸酯彩色涂料的研制.pdf
評論
0/150
提交評論