1、類別:全日制碩士研究生題目:高速電弧噴涂類別:全日制碩士研究生題目:高速電弧噴涂FeAlCr3C2復(fù)合涂層的性能研究英文題目:復(fù)合涂層的性能研究英文題目:PropertiesResearchofHVASFeAlCr3C2CompositCoatings研究生:孫二雄研究生:孫二雄學(xué)科名稱:材料學(xué)學(xué)科名稱:材料學(xué)指導(dǎo)教師:徐潤生指導(dǎo)教師:徐潤生教授級高級工程師教授級高級工程師二○○九年五月二○○九年五月碩士學(xué)位論文碩士學(xué)位論文分類號:學(xué)校

2、代碼:10128分類號:學(xué)校代碼:10128UDC:學(xué)號:20061261學(xué)號:20061261AbstractComparedtohighvelocityflamesprayingtechniqueshighvelocityarcsprayingtechnologyhassuchadvantagessuchas:highsprayingefficiencyenergysavingcosteffectivebetterautomatic

3、itcouldobtaingoodperfmancecoating.byadjustingthepowderofFe15Al45Cr3C2intheprocessofHVFSsixkindofdifferentcompoundcedwireswereobtained.Inthispresentwkhighvelocityarcspraying(HVAS)cedwiretechnologywasedtheintermetalliccoat

4、ingswithsupericrosionwearresistanceathightemperaturewerealsofoundItisagoodfoundationftheindustrialapplicationofthecoatinginfuture.Theadhesionstrengthmicrohardnesscrosionwearresistanceathightemperatureerosionwearresistanc

5、eathightemperaturefrictionwearbehaviourofsixFeAlCr3C2compositecoatingswereinvestigatedinthiswk.ThemphologyofcoatingswereobservedbySEMEDAXitsphasecompositionswereanalyzedbyXRD.Thecrosionerosiontheeffectmechanismofrareeart

6、hoxidationonthemwereinvestigated.Themainresultsofthiswkweresummarizedasfollows:Bymicrostructureanalysisitwasfoundthatthecompositecoatingpossessedtypicallaminatestructuretheposityunmeltedparticlesaswellaslargeflatsizepart

7、icleswithsmallamountinterfacecrackwereexistedinittheparticlesboundedverywellathinoxidationfilmexistedbetweenlargeflatsizelayersthereinfcementphaseCr3C2distributedunifmly.ThecompoundphasesmainlyincludedFe、Al、Cr3C2、Fe3AlFe

8、Al、FeCraswellassmallamountCe2Ni7.Theadhesionstrengthofthethreekindofcoatingswiththematrixwereallmethan33MPathehighestmicrohardnessreached444.32HVaswellas44.02HRC.Thecompositecoatingspossessbetterpropertyofhotcrosionresis

9、tance.Thecurveofcrosiondynamicsfollowsthedisciplinarianofparabolagenerally.Theweightgainsofthethreecompositecoatingswereabout67.25%、37.32%29.15%ofthe20Gsubstrateafter150hhotcrosionabout74.6%、41.4%、32.3%oftheFe15Al45Cr3C2

溫馨提示

  • 1. 本站所有資源如無特殊說明,都需要本地電腦安裝OFFICE2007和PDF閱讀器。圖紙軟件為CAD,CAXA,PROE,UG,SolidWorks等.壓縮文件請下載最新的WinRAR軟件解壓。
  • 2. 本站的文檔不包含任何第三方提供的附件圖紙等,如果需要附件,請聯(lián)系上傳者。文件的所有權(quán)益歸上傳用戶所有。
  • 3. 本站RAR壓縮包中若帶圖紙,網(wǎng)頁內(nèi)容里面會有圖紙預(yù)覽,若沒有圖紙預(yù)覽就沒有圖紙。
  • 4. 未經(jīng)權(quán)益所有人同意不得將文件中的內(nèi)容挪作商業(yè)或盈利用途。
  • 5. 眾賞文庫僅提供信息存儲空間,僅對用戶上傳內(nèi)容的表現(xiàn)方式做保護(hù)處理,對用戶上傳分享的文檔內(nèi)容本身不做任何修改或編輯,并不能對任何下載內(nèi)容負(fù)責(zé)。
  • 6. 下載文件中如有侵權(quán)或不適當(dāng)內(nèi)容,請與我們聯(lián)系,我們立即糾正。
  • 7. 本站不保證下載資源的準(zhǔn)確性、安全性和完整性, 同時也不承擔(dān)用戶因使用這些下載資源對自己和他人造成任何形式的傷害或損失。

最新文檔

評論

0/150

提交評論