1、<p>　　銦對(duì)可溶解合金溶解性能的影響</p><p><b>　　摘 要</b></p><p>　　本文以金屬鋁、銦及其他活化元素為原料，利用高溫熔融工藝制備了一種既具有一定溶解能力，又具有一定力學(xué)性能的新型高強(qiáng)功能鋁合金材料。通過不同溫度下的溶解實(shí)驗(yàn)，詳細(xì)研究了銦加入量對(duì)該材料溶解性能的影響，并通過X射線衍射（XRD)分析研究了該材料的物相組成。結(jié)果

2、表明，銦的加入量與溶解性能并不成線性關(guān)系，銦的加入量對(duì)鋁合金的溶解速率的影響有個(gè)臨界點(diǎn)，當(dāng)銦的量為0.4wt%時(shí)，溶解速率達(dá)到最大，當(dāng)銦的加入量繼續(xù)增加時(shí)，其對(duì)該材料的溶解性能的影響并不顯著。并對(duì)其溶解機(jī)理進(jìn)行了初步探索。</p><p>　　關(guān)鍵詞：可溶解合金材料，鋁合金，溶解性能，溶解機(jī)理</p><p>　　Study on Indium of soluble aluminum di

3、ssolved performance impact</p><p><b>　　ABSTRCT</b></p><p>　　A new aluminum alloy material with the property of mechanical and dissolve was fabricated through high temperature melting

4、 process. The best additives quantity of metal of Indium was get through dissolvable experiment and dissolvable curve.Meanwhile the reaction mechanism of dissolvable aluminum alloy material was investigated by X-ray diff

5、raction analysis (XRD) in detail.The result suggested that the amount of additive metal of Indium and the dissolvable property was not in diret ratio. As the</p><p>　　KEY WORDS: the dissolvable material, di